金属材料、复合材料疲劳和断裂相关试验标准汇总
- ASTM E739 线性或线性化应力-寿命(S-N)和应变-寿命(e-N)
- ASTM E468 Standard Practice for Presentation of Constant Amplitude Fatigue Test Results for Metallic Materials
- ASTM E466 金属材料力控制恒幅轴向疲劳试验方法
- ASTM E399 Standard Test Method for Linear-Elastic Plane-Strain Fracture Toughness of Metallic Material
- ASTM E561 Standard Test Method for K-R Curve Determination
- ASTM E740 Standard Practice for Fracture Testing with Surface-Crack Tension Specimens
- ASTM E1152 Standard Test Method for determining J-R Curves
- ASTM E1820 Standard Test Method for Measurement of Fracture Toughness
- ASTM E606/E606M Standard Test Method for Strain-Controlled Fatigue Testing
- ASTM E1942 Standard Guide for Evaluating Data Acquisition Systems Used in Cyclic Fatigue and Fracture Mechanics Testing
- ASTM E2472 Standard Test Method for Determination of Resistance to Stable Crack Extension under Low-Constraint Conditions
- ASTM B646 Standard Practice for Fracture Toughness Testing of luminum Alloys
- ASTM E2818 Standard Practice for Determination of Quasistatic Fracture Toughness of Welds
- GB/T 7732 金属材料表面裂纹拉伸试样断裂韧度试验方法
- GB/T 21143 金属材料准静态断裂韧度的统一试验方法
- GB/T 24176 金属材料疲劳试验数据统计方案与分析方法
- GB/T15248 金属材料轴向等幅低循环疲劳试验方法
- GB/T 4161 金属材料平面应变断裂韧度试验方法
- GB/T 26077 金属材料疲劳试验轴向应变控制方法
- GB/T 26076 金属薄板(带)轴向力控制疲劳试验方法
- GB/T 27595 胶粘剂结构胶粘剂拉伸剪切疲劳性能的试验方法
- GB/T 30064 金属材料钢构件断裂评估中裂纹尖端张开位移(CTOD)断裂韧度的拘束损失修正方法
- GB/T 24522 金属材料低拘束试样测定稳定裂纹扩展阻力的试验方法
- GB/T 28896 金属材料焊接接头准静态断裂韧度测定的试验方法
- GB/T 27551 金属材料焊缝破坏性试验断裂试验
- HB 6626 金属材料在含水介质中疲劳裂纹扩展速率试验方法
- HB 7572 金属材料(人字形缺口)平面应变断裂韧度试验方法
- HB 7680 金属材料高温疲劳裂纹扩展速率试验方法
- HB 7705 金属材料疲劳小裂纹扩展速率试验方法
- HB 7110 金属材料细节疲劳额定强度截止值(DFRcutoff)试验方法
- ASTM D5528 Standard Test Method for ModeI Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites
- ASTM D3479/D3479 MStandard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials
- ASTM D7774 Standard Test Method for Flexural Fatigue Properties of Plastics
- ASTM D7791 Standard Test Method for Uniaxial Fatigue Properties of Plastics
- ASTM D4482 Standard Test Method for Rubber Property-ExtensionCycling Fatigue
- ASTM D7615/D7615M Standard Practice for Open-Hole Fatigue Response of Polymer Matrix Composite Laminates
- ASTM D3166 Standard Test Method for Fatigue Properties of Adhesives in Shear by Tension Loading (Metal/Metal)
- ASTM D6115 Standard Test Method for ModeI Fatigue Delamination Growth Onset of Unidirectional Fiber-Reinforced Polymer atrixComposites
- ASTM E1049 Standard Practices for Cycle Counting in Fatigue Analysis
- GB/T 16779 纤维增强塑料层合板拉-拉疲劳性能试验方法
- GB/T 28891-2012 纤维增强塑料复合材料单向增强材料Ⅰ型层间断裂韧性的测定
- HB 7624 碳纤维复合材料层合板弯曲疲劳试验方法
- HB 7402 碳纤维复合材料层合板I型层间断裂韧性试验方法
- HB 7403 碳纤维复合材料层合板II型层间断裂韧性试验方法
- HB 7718.1 碳纤维复合材料层合板湿热环境下层间断裂韧性试验方法第1部分:I型层间断裂韧性试验方法
- HB 7718.2 碳纤维复合材料层合板湿热环境下层间断裂韧性试验方法第2部分:II型层间断裂韧性试验方法
- GJB 586 纤维增强塑料层板拉伸层间断裂韧性试验方法
- GJB 2637 碳纤维树脂基复合材料层合板疲劳试验方法
【免责声明】本文来自CAE仿真桃子叔叔,版权归原作者所有,仅用于学习等,对文中观点判断均保持中立,若您认为文中来源标注与事实不符,若有涉及版权等请告知,将及时修订删除,谢谢大家的关注!
著作权归作者所有,欢迎分享,未经许可,不得转载
首次发布时间:2023-07-03
最近编辑:1年前
硕士
|
CAE仿真负责人
个人著作《汽车NVH一本通》
获赞 1143粉丝 6105文章 924课程 20