Selective laser melting of silver submicron powder modified 316L stainless steel: Influence of silver addition on microstructures and performances

丨作者 南航顾冬冬教授团队

丨关键词

选区激光熔化；316L；Ag粉改性；显微组织；导电性；耐蚀性

丨论文要点

1.通过选区激光熔化技术制备出Ag/316L不锈钢纳米复合材料

2.研究了银的添加对选区激光熔化成形316L不锈钢复合材料跨尺度显微组织和导电性及耐蚀性的影响

3.揭示了Ag对316L不锈钢的耐蚀性和导电性的影响机理

丨Highlights

2.Selective laser melting was employed to fabricated 316L + Ag composite.

3.The influence of Ag addition on multiscale microstructures was investigated.

4.The SLMed 316L + Ag samples exhibited enhanced electrical and corrosion performance

丨Graphical abstract

       

丨主要内容

316L不锈钢优异的耐蚀性和低成本使其广泛用于医疗、食品加工、燃料电池双极板等领域，然而单纯的316L不锈钢的耐蚀性还不能满足某些特殊工况的工业要求。本文通过选区激光熔化技术，将银添加到316L不锈钢的基体中，最终得到Ag/316L纳米复合材料。研究了Ag对316L不锈钢微观组织的影响和Ag/316L纳米复合材料的耐蚀性和导电性。

       

丨引用格式

Jingfeng Quan, Kaijie Lin, Dongdong Gu. Selective laser melting of silver submicron powder modified 316L stainless steel: Influence of silver addition on microstructures and performances. Powder technol 364(2020)478-483.

丨相关项目

国家自然科学基金 编号51905269

江苏省青年自然基金 编号BK20170787

丨原文下载

长按复 制浏览器打开

https://doi.org/10.1016/j.powtec.2020.01.082