International Journal of Solids and Structures

Prediction and Demonstration of Periodic Tensile Cracking in Rate-Dependent Porous Cement

Lu Yunxing, Veveakis Manolis, Crandall Dustin, Bunger Andrew P.

doi:10.1016/j.ijsolstr.2023.112527

速率相关多孔水泥周期性拉伸开裂的预测与论证

Periodic tensile cracks are shown to occur when cylinder-shaped saturated cement specimens are subjected to rapid decompression, with the spacing between the cracks scaling as a power law of the decompression time. This behavior is predicted by theory, which is specified to this scenario based on prior work that was more general and applied to compaction bands. Specifically, the formation of the tensile cracks is shown to coincide with periodicity that naturally arises in the effective stress when the material follows a Terzaghi-type consolidation law, although in reverse for dilation and with material deformation described by a rate-dependent viscoplastic law. When strain rate is proportional to effective stress to a power that is greater than one, periodic regions of tensile effective stress arise through the poromechanical fluid-solid coupling. The theoretically-predicted exponent of the resulting power-law relationship between tensile cracks spacing and unloading time successfully brackets the experimental results, for which it is observed that the exponent is slightly stronger than a square-root relationship (0.28 to 0.67) at testing temperatures of 20 ℃ and 90 ℃. These results demonstrate that rapid-depressurization leads to periodic fracturing that could, on the one hand, be detrimental to the isolation provided by cement used to seal wellbores in the petroleum industry. On the other hand, the periodic tensile cracks could also be favorable to production if generated in low-permeability reservoir rocks such as shales that are targeted for petroleum production or granites that are targeted for geothermal energy.

柱状饱和水泥试样在快速减压过程中出现周期性拉伸裂缝,裂缝间距随减压时间呈幂律变化。这种行为是由理论预测的,这是基于先前的工作而指定的,这些工作更一般,并应用于压实带。具体来说,拉伸裂纹的形成与材料遵循terzaghi型固结规律时自然产生的有效应力的周期性相一致,尽管与膨胀和材料变形由速率相关的粘塑性规律描述相反。当应变率与有效应力成正比且大于1时,通过孔隙力学流固耦合会出现拉有效应力的周期性区域。拉伸裂纹间距与卸载时间幂律关系的理论预测指数与实验结果相吻合,在20℃和90℃的试验温度下,该指数略强于平方根关系(0.28 ~ 0.67)。这些结果表明,快速降压导致周期性压裂,这一方面可能不利于石油工业中用于密封井眼的水泥提供的隔离。另一方面,周期性张性裂缝如果产生于低渗透储层岩石中,如以石油生产为目标的页岩或以地热能为目标的花岗岩,也可能有利于生产。


Journal of the Mechanics and Physics of Solids

Delayed fracture caused by time-dependent damage in PDMS

Wang Jikun, Zhu Bangguo, Hui Chung-Yuen, Zehnder Alan T.

doi:10.1016/j.jmps.2023.105459

PDMS时间依赖性损伤引起的迟发性骨折

An experimental and theoretical study of delayed fracture of polydimethlsiloxane (PDMS) is presented. Previous works have demonstrated that delayed fracture in single edge notch specimens is caused by time dependent damage due to chain scission. Here we study the interactions between damage and the elastic field using different specimens and crack geometries with blunt and sharp cracks. Our experiments show that initial toughness is not well defined, as stable slow crack growth can occur over a range of applied loads. Our experiments demonstrate that there is a universal relation between crack growth rate and applied energy release rate. A model coupling the nonlinear elastic deformation and rate dependent bond scission is proposed and is in good agreement with experimental data.

对聚二甲基硅氧烷(PDMS)的延迟断裂进行了实验和理论研究。以往的研究表明,单刃缺口试样的延迟断裂是由链断裂引起的时间依赖性损伤引起的。本文采用不同的试样和裂纹几何形状研究了损伤与弹性场之间的相互作用。我们的实验表明,初始韧性不是很好地定义,因为稳定的缓慢裂纹扩展可以在一定范围内发生。实验表明,裂纹扩展速率与外加能释放速率之间存在普遍的关系。提出了一个耦合非线性弹性变形和速率相关键断的模型,该模型与实验数据吻合较好。


A phase-field formulation for cohesive fracture based on the Park-Paulino-Roesler (PPR) cohesive fracture model

Giraldo-Londoño Oliver, Muñetón-López Rogelio A.

doi:10.1016/j.jmps.2023.105460

基于Park-Paulino-Roesler (PPR)黏性断裂模型的黏性断裂相场公式

Unlike most cohesive zone models (CZMs), the Park-Paulino-Roesler (PPR) cohesive fracture model has the inherent ability to control the softening shape of the traction-separation relationships, which makes it suitable to model fracture for a wide variety of materials. Like other CZMs, the PPR model is well-suited for problems where the crack path is known a priori but its implementation may become complex in situations where the crack path is not known beforehand. To overcome this limitation, we recast the PPR model within the framework of the phase field method, which enables the modeling of crack propagation problems with complex crack topologies using a straightforward multi-field finite element implementation. We use constitutive functions (i.e., crack geometric function and degradation function) consistent with the PPR model for the case of mode-I fracture, such that equivalent traction-separation relationships from the phase-field model approximate those from the original PPR model. Our choice of geometric and degradation functions is based upon those proposed by Wu (2017). We present several numerical examples to demonstrate the ability of the model to capture fracture of problems with different materials, geometries, and boundary conditions. Also, we show that the results from our model converge to those obtained with the original PPR model for problems where the crack path is known a priori. Being crucial in engineering design, we finally show that the model can capture size and boundary effects with satisfactory accuracy.

与大多数黏结带模型(CZMs)不同,Park-Paulino-Roesler (PPR)黏结断裂模型具有固有的控制牵引-分离关系软化形状的能力,这使得它适用于各种材料的断裂模型。与其他czm一样,PPR模型非常适合于裂纹路径先验已知的问题,但在裂纹路径事先未知的情况下,其实现可能会变得复杂。为了克服这一限制,我们在相场方法的框架内重新构建了PPR模型,这使得能够使用简单的多场有限元实现对具有复杂裂纹拓扑结构的裂纹扩展问题进行建模。对于i型断裂,我们使用了与PPR模型一致的本构函数(即裂纹几何函数和退化函数),使得相场模型的等效牵引-分离关系近似于原始PPR模型。我们对几何函数和退化函数的选择是基于Wu(2017)提出的。我们提出了几个数值例子来证明该模型能够捕获具有不同材料,几何形状和边界条件的断裂问题。此外,我们还表明,对于已知先验裂纹路径的问题,我们的模型的结果收敛于原始PPR模型的结果。在工程设计中至关重要的是,我们最终证明了该模型能够以令人满意的精度捕获尺寸和边界效应。


Mechanics of Materials

Modelling the effect of layer strength distribution on the brick-and-mortar failure regimes and properties

Hunter Georgia, Djumas Lee, Molotnikov Andrey, Brassart Laurence

doi:10.1016/j.mechmat.2023.104820

模拟了层间强度分布对砂浆破坏形态和性能的影响

Brick-and-Mortar structures are of high interest because their staggered multi-material arrangement can result in a remarkable combination of high strength and high toughness. Synthetic replication of these structures with high geometric control has been made possible recently with the advances in multi-material Additive Manufacturing (AM). However, very little is known on how inherent material variation in the constituent materials, which can be significant in AM, affects the structure response. In this work, we use a semi-analytical model to theoretically show that a variation in the strength of the layers in a Brick-and-Mortar structure has a significant effect on the failure response of the structure. It can lead to changes in failure regimes and negatively impact the mechanical properties, such as decrease the strain to failure or decrease the yield stress. This is particularly pronounced when the material behaviour is situated close to the transition point between failure regimes. We then present an experimental method to capture strength variability in the layer material and demonstrate that the incorporation of this variability into the semi-analytical model improves our prediction of the failure response of the structure, as compared to experiments.

砖和砂浆结构是高度感兴趣的,因为它们交错的多材料排列可以导致高强度和高韧性的显着组合。近年来,随着多材料增材制造(AM)技术的进步,具有高度几何控制的这些结构的合成复 制成为可能。然而,对于组成材料的固有材料变化如何影响结构响应知之甚少,这在AM中可能很重要。在这项工作中,我们使用半解析模型从理论上表明,砖混结构中各层强度的变化对结构的破坏响应有显著影响。它可以导致失效状态的改变,并对力学性能产生负面影响,例如降低失效应变或降低屈服应力。当材料行为接近失效状态之间的过渡点时,这一点尤为明显。然后,我们提出了一种实验方法来捕获层材料中的强度变异性,并证明与实验相比,将这种变异性纳入半解析模型可以提高我们对结构破坏响应的预测。


International Journal of Plasticity

Transformation Induced Plasticity in Ferritic Steels: New Experiments and Updated Modeling

Taleb Lakhdar, Duchaussoy Amandine, Jimenez Jose

doi:10.1016/j.ijplas.2023.103775

铁素体钢的相变诱发塑性:新的实验和更新的模型

In this work, we first experimentally investigated transformation-induced plasticity (TRIP) in the martensitic transformation of 36NiCrMo steel. The objective was to study some loading conditions encountered in industrial applications such as quenching and multi-pass welding. In addition to the classical case where the applied loading was maintained constant during the transformation, original TRIP experiments were performed with more complex applied loading: cyclic, multi-axial, proportional, nonproportional, applied during only a part of the transformation, high up to the yield stress of the austenitic phase. The test results showed a dissymmetry between the TRIP responses under tension and compression and reveal the existence of TRIP backstress. Finally, we have found an approximation of the maximum amount of TRIP which may be obtained for the transformation in the material under question (about 1.1% in our case). This result suggests that for a first approximation, the amount of final TRIP may be considered proportional to the norm of the applied stress as long as the latter does not exceed the yield stress. Some microstructural investigations have been performed in order to quantify the phase constituents and study the effect of the TRIP test conditions on the microstructure. The next step of the work was devoted to TRIP modeling where the model of Leblond (1989) and its extension by Taleb and Sidoroff (2003) have been considered. From the simulation of the classical TRIP tests described above, it was found that this model generally overestimates the TRIP strain and contrary to experiments, it predicts the same TRIP norm under tension and equivalent compression. Thus, maintaining the practicality of the original version and its ease of use, a new version of the model is proposed having the capabilities to describe the phenomena observed experimentally. Namely, the general overestimation of TRIP has been corrected by the introduction of the TRIP backstress effects, while the dissymmetry tension-compression was corrected through the introduction of a function of the first invariant applied stress tensor. The new version of the model shows excellent capabilities in simulating the experimental data base performed in this work. Nevertheless, further research considering other steels and other transformations is warranted.

在这项工作中,我们首先实验研究了36NiCrMo钢马氏体相变中的相变诱导塑性(TRIP)。目的是研究工业应用中遇到的一些加载条件,如淬火和多道次焊接。除了在转变过程中施加恒定载荷的经典情况外,原始TRIP实验还进行了更复杂的施加载荷:循环,多轴,比例,非比例,仅在转变的一部分施加载荷,高至奥氏体相的屈服应力。试验结果表明,拉伸和压缩作用下的TRIP响应不对称,表明TRIP背应力的存在。最后,我们已经找到了在所讨论的材料中可能获得的最大TRIP量的近似值(在我们的情况下约为1.1%)。这一结果表明,对于第一个近似,最终的TRIP量可以被认为与施加应力的规范成正比,只要后者不超过屈服应力。为了量化相组成和研究TRIP试验条件对微观组织的影响,进行了一些显微组织研究。下一步的工作是致力于TRIP建模,其中考虑了Leblond(1989)的模型及其Taleb和Sidoroff(2003)的扩展。通过对上述经典TRIP试验的模拟发现,该模型普遍高估了TRIP应变,与实验相反,它预测的是相同的拉伸和等效压缩下的TRIP范数。因此,在保持原始版本的实用性和易用性的基础上,提出了一个能够描述实验观察到的现象的新版本模型。即,通过引入TRIP背应力效应纠正了TRIP的一般高估,而通过引入第一个不变施加应力张量的函数纠正了不对称的张压。新版本的模型在模拟本工作的实验数据库方面表现出优异的能力。然而,进一步的研究考虑其他钢和其他转化是必要的。


Void nucleation at dislocation boundaries aided by the synergy of multiple dislocation pile-ups

Yang Ping, Zhao Pengyang

doi:10.1016/j.ijplas.2023.103779

在多个位错堆积的协同作用下,位错边界处的空洞成核

Void nucleation is of great significance in understanding ductile fracture. Recent experiments have shown that voids are nucleated via vacancy condensation and dislocation boundaries are the main nucleation sites. However, it is unclear what role is played exactly by dislocation boundaries in promoting void nucleation. Here we propose a new mechanism for dislocation boundary-induced void nucleation and develop a corresponding model based on the classical nucleation theory and vacancy diffusion theory. The model suggests that void nucleation is mainly influenced by hydrostatic stress, temperature, and relative vacancy concentration, whose contributions are systematically studied. It is also suggested that the vacancy formation energy and the interaction energy of hydrostatic stress and vacancy, which are absent in the previous models and introduced in ours, exhibit a clear tendency to lower the activation free energy barrier. Analysis of the nucleation kinetic suggests that the growth rate of void depends on the vacancy diffusion coefficient and vacancy concentration; the higher the values of these parameters, the faster the growth rate of the void. The kinetic feasibility of the newly proposed mechanism is examined using three-dimensional discrete dislocation dynamics simulations. The results predict that the size of incipient voids nucleated at the dislocation boundary is ∼35 nm, which is consistent with the experimental characterization value of ∼50 nm. Finally, when the relaxation of the dislocation boundary is considered, the synergistic effect is weakened.

空洞成核对认识韧性断裂具有重要意义。最近的实验表明,孔洞通过空位凝聚成核,位错边界是主要的成核位置。然而,目前还不清楚位错边界在促进空洞成核过程中究竟起着怎样的作用。本文在经典成核理论和空位扩散理论的基础上,提出了位错边界诱导空洞成核的新机制,并建立了相应的模型。该模型表明,孔隙成核主要受静水应力、温度和相对空位浓度的影响,并对其贡献进行了系统研究。此外,本文还引入了前人模型中所没有的空位形成能和静水应力与空位的相互作用能,它们具有明显的降低激活自由能垒的趋势。成核动力学分析表明,空穴的生长速率取决于空位扩散系数和空位浓度;这些参数的值越高,孔隙的生长速度越快。采用三维离散位错动力学模拟验证了新提出的机理的动力学可行性。结果预测,在位错边界处初始孔洞的成核尺寸为~ 35 nm,与实验表征值~ 50 nm一致。最后,当考虑位错边界松弛时,协同效应减弱。


Thin-Walled Structures

Thermal and mechanical damage to carbon fibre reinforced composites with metallic fasteners under lightning strike

Kuang Chengzhao, Zhou Yuchen, Zhu Huixin, Shi Qizhen, Fu Kunkun, Li Yan

doi:10.1016/j.tws.2023.111280

带有金属紧固件的碳纤维增强复合材料在雷击下的热损伤和机械损伤

In this study, lightning strike (LS) damage to carbon fibre reinforced composites (CFRCs) with metallic fasteners was investigated by simulated LS tests and finite element (FE) model. First, the LS damage mode and mechanism of a single-lap composite joint and a CFRC laminate with a metallic rivet were studied. Resin pyrolysis was found on the surface but severe delamination was evident inside the composites due to a gas explosion caused by the sudden burn-off of polymer matrices and thermal expansion inside the laminate. Then, the effect of rivet spacing on the LS damage to CFRCs was examined. The results showed that the damaged area was significantly reduced because the surrounding rivets effectively suppressed impact-induced delamination and consumed more electrical energy. The results also showed that large-area delamination across the rivets was achieved due to high potential at the surrounding rivets when the spacing was short but dynamic deflection was confined by the surrounding rivets. In contrast, delamination was only concentrated at the central rivet when the spacing was large, which can be ascribed to fewer currents flowing into the surrounding rivets, and the confinement of the adjacent rivets was less significant.

采用模拟雷击试验和有限元模型研究了金属紧固件碳纤维增强复合材料的雷击损伤。首先,研究了单搭接复合材料节点和金属铆钉CFRC层合板的LS损伤模式和机理。表面发现了树脂热解,但由于聚合物基体突然燃烧和层合板内部热膨胀引起的气体爆炸,复合材料内部明显存在严重的分层现象。然后,研究了铆钉间距对CFRCs的LS损伤的影响。结果表明,由于周围铆钉有效地抑制了冲击引起的分层,并且消耗了更多的电能,因此损伤面积显著减小。结果还表明,当铆钉间距较短但动态挠度受到周围铆钉的限制时,由于周围铆钉的高电位,铆钉之间会发生大面积的分层。相反,当间距较大时,分层只集中在中心铆钉上,这可以归因于流入周围铆钉的电流较少,相邻铆钉的限制不太明显。



来源:复合材料力学仿真Composites FEM
ACTMechanicalAdditiveSystemDeform断裂复合材料非线性燃烧增材焊接裂纹理论爆炸材料控制
著作权归作者所有,欢迎分享,未经许可,不得转载
首次发布时间:2024-11-03
最近编辑:13天前
Tansu
签名征集中
获赞 3粉丝 0文章 503课程 0
点赞
收藏
作者推荐

【新文速递】2023年10月17日固体力学SCI期刊最新文章

今日更新:Journal of the Mechanics and Physics of Solids 2 篇,Mechanics of Materials 1 篇Journal of the Mechanics and Physics of SolidsA unified strength criterion for two-dimensional materials via bond failure analysisZhang Guoqiang, Chen Yan, Yue Shengying, Zhang Yong-Wei, Qin Huasong, Liu Yilundoi:10.1016/j.jmps.2023.105466通过粘接破坏分析得出二维材料的统一强度标准The family of two-dimensional (2D) materials, including graphene, hexagonal boron nitride, transition metal dichalcogenides, and others, exhibits a wide range of lattice structures and defect configurations, leading to complex deformation mechanisms and mechanical failure behaviors. However, there is currently no universally accepted criterion that accurately describes the mechanical failures of these materials. In this study, we aim to address this issue by introducing the concept of intrinsic bond strength, which is solely dependent on the local chemical environment of the bond and is independent of loading states, defect types, and fracture bonds. We demonstrate the existence of this intrinsic bond strength and propose a unified strength criterion that considers the balance between the intrinsic bond strength and local stress state for any 2D material. By employing this unified strength criterion, we are able to accurately predict the failure of various 2D materials with different types of defects, including voids, cracks, grain boundaries, and hydrogenation. This work resolves a long-standing issue in predicting the mechanical failure of 2D materials via bond failure analysis, and carries important implications for the design and development of 2D materials with enhanced mechanical properties.二维(2D)材料家族,包括石墨烯、六方氮化硼、过渡金属二卤化物等,呈现出多种多样的晶格结构和缺陷构型,导致复杂的变形机制和机械失效行为。然而,目前还没有一个普遍接受的标准来准确描述这些材料的机械失效。在本研究中,我们旨在通过引入本征键强度的概念来解决这一问题,本征键强度完全取决于键的局部化学环境,与加载状态、缺陷类型和断裂键无关。我们证明了本征结合强度的存在,并提出了一种统一的强度准则,该准则考虑了任何二维材料的本征结合强度和局部应力状态之间的平衡。通过采用这一统一强度准则,我们能够准确预测具有不同类型缺陷(包括空隙、裂纹、晶界和氢化)的各种二维材料的失效。这项工作解决了长期以来通过键合失效分析预测二维材料力学失效的问题,对设计和开发具有更强力学性能的二维材料具有重要意义。What are the “dispersive shear bands” on the surfaces of layered heterostructured materials?Ma Huwen, Zhao Yanchun, Lyu Zhi, Wang Xue, Zhu Yuntian, Gao Yanfeidoi:10.1016/j.jmps.2023.105467 什么是层状异质结构材料表面的 "分散剪切带"?Hetero-deformation-induced (HDI) strengthening mechanism has been well investigated in heterostructured materials including layered/gradient materials prepared by surface attrition or other processing techniques. While the roles played by the geometrically necessary dislocations (GNDs) and the forward/back stresses on the grain scale have been a focus in nearly all these studies, some latest works reveal the peculiar formation of “dispersive shear bands” or strain localizations on the surfaces of layered/gradient materials. Feature sizes of these “shear bands” are commensurate with the macroscopic sample size, but not on the microstructural length scales, thus excluding the HDI strengthening as the primary mechanism. In this work, using a sandwich structure as an illustrative example, we demonstrate that the origin of these shear bands be localized necking with intermediate wavelengths and inclined orientations, which are critically dictated by the hardening behavior of the constituent layers, the geometric parameters, and the initial morphological perturbations. The layered structure under tension may not neck with an infinite wavelength (i.e., the Considère mode), but neck at intermediate wavelengths which actually correspond to a much larger uniform ductility than the commonly observed Considère necking mode. The arrangements of these shear bands can be further classified as I, X, and W types. Findings in this work not only resolve the origin of recent unusual experimental observations, but also suggest an alternative way of understanding and improving the ductility in heterostructured materials.异质形变诱导(HDI)强化机制已在异质结构材料中得到深入研究,包括通过表面损耗或其他加工技术制备的层状/梯度材料。几乎所有这些研究都重点关注了几何必要位错(GNDs)和晶粒尺度上的前向/后向应力所发挥的作用,而一些最新研究则揭示了层状/梯度材料表面 "分散剪切带 "或应变定位的奇特形成。这些 "剪切带 "的特征尺寸与宏观样品尺寸相称,但与微观结构长度尺度不符,因此排除了高密度互联强化作为主要机制的可能性。在这项工作中,我们以三明治结构为例,证明了这些剪切带的起源是具有中间波长和倾斜方向的局部颈缩,这主要由组成层的硬化行为、几何参数和初始形态扰动决定。张力作用下的层状结构可能不会以无穷大的波长(即康西代尔模式)出现缩颈,而是以中间波长出现缩颈,这实际上对应于比通常观察到的康西代尔缩颈模式大得多的均匀延展性。这些剪切带的排列可进一步分为 I、X 和 W 三种类型。这项工作的发现不仅解决了近期不寻常实验观测的起源问题,还为理解和改进异质结构材料的延展性提出了另一种方法。Mechanics of Materials4D local investigation of mechanical behavior of open-cell foams by enhanced morphological analysis and microstructure-adapted digital volume correlation for tribology applicationsLacaj E., Doumalin P., Bouyer J., Jolly P., Henry Y., Fatu A., Beaudoin A., Ennazii A.-E., Couderc B., King A.doi:10.1016/j.mechmat.2023.104836通过增强形态分析和微结构适配数字体积相关性对开孔泡沫的机械行为进行四维局部研究,以促进摩擦学应用In ex-poro-hydrodynamic (XPHD) lubrication, fluid impregnated, open-cell elastomer foams constitute a composite material aiming to improve the load carrying and damping capacity of lubricated systems and to provide more environmentally sustainable solutions. The performance of XPHD-based devices depends on the interactions between solid and fluid phases, occurring and evolving simultaneously during dynamic compression of an imbibed foam. Even at normal regimes, the foam microstructure undergoes large deformations and is prone to strain concentrations which modify its local porosity and influence the mechanical behavior of the composite. In this context, this work focuses on the development of a systematic and accurate characterization technique for describing the main morphological changes happening under uniaxial compression of a high porosity dry open-cell polyurethane foam, by in-situ X-ray microtomography (μCT) testing. A combination of 3D image analysis and digital volume correlation (DVC) is considered to identify and trace the spatial and temporal location of key microstructural features at every loaded state. In this way, the detailed transformations of cells and pores obtained by this method are presented here to give further insight into the deformation mechanisms involved. Then, the advantages and the limits of the overall methodology in analyzing high porosity open-cell foams are regarded in terms of feature segmentation and measurement precision. Both a classic and a microstructure-adapted DVC are compared at their respective scales, and finally their sensibility to emphasize local strain heterogeneities is discussed.在孔外流体动力(XPHD)润滑中,流体浸渍开孔弹性泡沫构成了一种复合材料,旨在提高润滑系统的承载能力和阻尼能力,并提供更具环境可持续性的解决方案。基于 XPHD 的设备的性能取决于固相和流体相之间的相互作用,这种相互作用在浸泡泡沫的动态压缩过程中同时发生和发展。即使在正常状态下,泡沫微观结构也会发生较大变形,并容易产生应变集中,从而改变局部孔隙率,影响复合材料的机械行为。在这种情况下,这项工作的重点是开发一种系统而精确的表征技术,通过原位 X 射线显微层析(μCT)测试,描述高孔隙率干法开孔聚氨酯泡沫在单轴压缩下发生的主要形态变化。三维图像分析和数字体积相关(DVC)相结合,可识别和追踪每个加载状态下关键微观结构特征的空间和时间位置。因此,本文介绍了该方法获得的细胞和孔隙的详细变化,以便进一步了解相关的变形机制。然后,从特征分割和测量精度的角度,探讨了分析高孔隙率开孔泡沫的整体方法的优势和局限性。比较了经典 DVC 和微结构适应 DVC 各自的尺度,最后讨论了它们对强调局部应变异质性的敏感性。来源:复合材料力学仿真Composites FEM

未登录
还没有评论
课程
培训
服务
行家
VIP会员 学习 福利任务 兑换礼品
下载APP
联系我们
帮助与反馈